304 ati 316 SS capillary Coil Tubes olupese ni china
304 ati 316 SS capillary Coil Tubes olupese ni china
Awọn onipò ohun elo oriṣiriṣi lo wa ti a lo fun ọpọn iwẹ fun awọn paarọ ooru, awọn igbona, awọn igbona nla ati awọn ohun elo otutu giga miiran ti o kan alapapo tabi itutu agbaiye.Awọn oriṣi oriṣiriṣi pẹlu ọpọn irin alagbara irin 3/8 ti o ni wiwọ daradara.Ti o da lori iru ohun elo naa, iru omi ti o tan kaakiri nipasẹ awọn tubes ati awọn ipele ohun elo, iru awọn tubes yatọ.Awọn iwọn oriṣiriṣi meji wa fun awọn tubes ti a fi sinu bi iwọn ila opin tube ati iwọn ila opin ti okun, ipari gigun, sisanra ogiri ati awọn iṣeto.Awọn tubes Coil SS ni a lo ni awọn iwọn oriṣiriṣi ati awọn onipò da lori awọn ibeere ohun elo.Awọn ohun elo alloy giga ati awọn ohun elo irin erogba miiran ti o wa fun ọpọn okun bi daradara.
Ibamu Kemikali ti Ọpa Ti Awọ-Aiyẹfun Alailowaya
| Ipele | C | Mn | Si | P | S | Cr | Mo | Ni | N | Ti | Fe | |
| 304 | min. | 18.0 | 8.0 | |||||||||
| o pọju. | 0.08 | 2.0 | 0.75 | 0.045 | 0.030 | 20.0 | 10.5 | 0.10 | ||||
| 304L | min. | 18.0 | 8.0 | |||||||||
| o pọju. | 0.030 | 2.0 | 0.75 | 0.045 | 0.030 | 20.0 | 12.0 | 0.10 | ||||
| 304H | min. | 0.04 | 18.0 | 8.0 | ||||||||
| o pọju. | 0.010 | 2.0 | 0.75 | 0.045 | 0.030 | 20.0 | 10.5 | |||||
| SS 310 | ti o pọju 0.015 | 2 o pọju | ti o pọju 0.015 | ti o pọju 0.020 | ti o pọju 0.015 | 24.00 26.00 | 0.10 ti o pọju | 19.00 21.00 | 54.7 iṣẹju | |||
| SS 310S | ti o pọju 0.08 | 2 o pọju | 1.00 ti o pọju | ti o pọju 0.045 | ti o pọju 0.030 | 24.00 26.00 | ti o pọju 0.75 | 19.00 21.00 | 53.095 iṣẹju | |||
| SS 310H | 0.04 0.10 | 2 o pọju | 1.00 ti o pọju | ti o pọju 0.045 | ti o pọju 0.030 | 24.00 26.00 | 19.00 21.00 | 53.885 iṣẹju | ||||
| 316 | min. | 16.0 | 2.03.0 | 10.0 | ||||||||
| o pọju. | 0.035 | 2.0 | 0.75 | 0.045 | 0.030 | 18.0 | 14.0 | |||||
| 316L | min. | 16.0 | 2.03.0 | 10.0 | ||||||||
| o pọju. | 0.035 | 2.0 | 0.75 | 0.045 | 0.030 | 18.0 | 14.0 | |||||
| 316TI | ti o pọju 0.08 | 10.00 14.00 | 2.0 ti o pọju | ti o pọju 0.045 | ti o pọju 0.030 | 16.00 18.00 | ti o pọju 0.75 | 2.00 3.00 | ||||
| 317 | ti o pọju 0.08 | 2 o pọju | 1 o pọju | ti o pọju 0.045 | ti o pọju 0.030 | 18.00 20.00 | 3.00 4.00 | 57.845 iṣẹju | ||||
| SS 317L | ti o pọju 0.035 | 2.0 ti o pọju | 1.0 ti o pọju | ti o pọju 0.045 | ti o pọju 0.030 | 18.00 20.00 | 3.00 4.00 | 11.00 15.00 | 57.89 iṣẹju | |||
| SS 321 | ti o pọju 0.08 | 2.0 ti o pọju | 1.0 ti o pọju | ti o pọju 0.045 | ti o pọju 0.030 | 17.00 19.00 | 9.00 12.00 | 0.10 ti o pọju | 5 (C + N) 0,70 max | |||
| SS 321H | 0.04 0.10 | 2.0 ti o pọju | 1.0 ti o pọju | ti o pọju 0.045 | ti o pọju 0.030 | 17.00 19.00 | 9.00 12.00 | 0.10 ti o pọju | 4 (C + N) 0,70 max | |||
| 347/ 347H | ti o pọju 0.08 | 2.0 ti o pọju | 1.0 ti o pọju | ti o pọju 0.045 | ti o pọju 0.030 | 17.00 20.00 | 9.0013.00 | |||||
| 410 | min. | 11.5 | ||||||||||
| o pọju. | 0.15 | 1.0 | 1.00 | 0.040 | 0.030 | 13.5 | 0.75 | |||||
| 446 | min. | 23.0 | 0.10 | |||||||||
| o pọju. | 0.2 | 1.5 | 0.75 | 0.040 | 0.030 | 30.0 | 0.50 | 0.25 | ||||
| 904L | min. | 19.0 | 4.00 | 23.00 | 0.10 | |||||||
| o pọju. | 0.20 | 2.00 | 1.00 | 0.045 | 0.035 | 23.0 | 5.00 | 28.00 | 0.25 | |||
Mechanical Properties Chart of Alagbara Irin Tubing Coil
| Ipele | iwuwo | Ojuami Iyo | Agbara fifẹ | Agbara ikore (0.2% aiṣedeede) | Ilọsiwaju |
| 304/304L | 8.0 g / cm3 | 1400°C (2550°F) | Psi 75000, MPa 515 | Psi 30000, MPa 205 | 35% |
| 304H | 8.0 g / cm3 | 1400°C (2550°F) | Psi 75000, MPa 515 | Psi 30000, MPa 205 | 40% |
| 310 / 310S / 310H | 7.9 g/cm3 | 1402°C (2555°F) | Psi 75000, MPa 515 | Psi 30000, MPa 205 | 40% |
| 306/ 316H | 8.0 g / cm3 | 1400°C (2550°F) | Psi 75000, MPa 515 | Psi 30000, MPa 205 | 35% |
| 316L | 8.0 g / cm3 | 1399°C (2550°F) | Psi 75000, MPa 515 | Psi 30000, MPa 205 | 35% |
| 317 | 7.9 g/cm3 | 1400°C (2550°F) | Psi 75000, MPa 515 | Psi 30000, MPa 205 | 35% |
| 321 | 8.0 g / cm3 | 1457°C (2650°F) | Psi 75000, MPa 515 | Psi 30000, MPa 205 | 35% |
| 347 | 8.0 g / cm3 | 1454°C (2650°F) | Psi 75000, MPa 515 | Psi 30000, MPa 205 | 35% |
| 904L | 7,95 g / cm3 | 1350°C (2460°F) | Psi 71000, MPa 490 | Psi 32000 , MPa 220 | 35% |
SS Oluyipada Ooru Kikun Awọn tubes Awọn ipele deede
| ITOJU | WORKSTOFF NR. | UNS | JIS | BS | GOST | AFNOR | EN |
| SS 304 | 1.4301 | S30400 | SUS 304 | 304S31 | 08Х18Н10 | Z7CN18-09 | X5CrNi18-10 |
| SS 304L | 1.4306 / 1.4307 | S30403 | SUS 304L | 3304S11 | 03Х18Н11 | Z3CN18-10 | X2CrNi18-9 / X2CrNi19-11 |
| SS 304H | 1.4301 | S30409 | – | – | – | – | – |
| SS 310 | 1.4841 | S31000 | SUS 310 | 310S24 | 20Ch25N20S2 | – | X15CrNi25-20 |
| SS 310S | 1.4845 | S31008 | SUS 310S | 310S16 | 20Ch23N18 | – | X8CrNi25-21 |
| SS 310H | – | S31009 | – | – | – | – | – |
| SS 316 | 1.4401 / 1.4436 | S31600 | SUS 316 | 316S31 / 316S33 | – | Z7CND17-11-02 | X5CrNiMo17-12-2 / X3CrNiMo17-13-3 |
| SS 316L | 1.4404 / 1.4435 | S31603 | SUS 316L | 316S11 / 316S13 | 03Ch17N14M3 / 03Ch17N14M2 | Z3CND17-11-02 / Z3CND18-14-03 | X2CrNiMo17-12-2 / X2CrNiMo18-14-3 |
| SS 316H | 1.4401 | S31609 | – | – | – | – | – |
| SS 316Ti | 1.4571 | S31635 | SUS 316Ti | 320S31 | 08Ch17N13M2T | Z6CNDT17-123 | X6CrNiMoTi17-12-2 |
| SS 317 | 1.4449 | S31700 | SUS 317 | – | – | – | – |
| SS 317L | 1.4438 | S31703 | SUS 317L | – | – | – | X2CrNiMo18-15-4 |
| SS 321 | 1.4541 | S32100 | SUS 321 | – | – | – | X6CrNiTi18-10 |
| SS 321H | 1.4878 | S32109 | SUS 321H | – | – | – | X12CrNiTi18-9 |
| SS 347 | 1.4550 | S34700 | SUS 347 | – | 08Ch18N12B | – | X6CrNiNb18-10 |
| SS 347H | 1.4961 | S34709 | SUS 347H | – | – | – | X6CrNiNb18-12 |
| SS 904L | 1.4539 | N08904 | SUS 904L | 904S13 | STS 317J5L | Z2 NCDU 25-20 | X1NiCrMoCu25-20-5 |